AISI 310Cb Stainless Steel vs. ASTM Grade LC9 Steel

Both AISI 310Cb stainless steel and ASTM grade LC9 steel are iron alloys. They have 62% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AISI 310Cb stainless steel and the bottom bar is ASTM grade LC9 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
22
Fatigue Strength, MPa 200
420
Poisson's Ratio 0.28
0.29
Reduction in Area, % 46
34
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 580
660
Tensile Strength: Yield (Proof), MPa 230
590

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1100
430
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
10

Otherwise Unclassified Properties

Base Metal Price, % relative 28
8.0
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.8
2.3
Embodied Energy, MJ/kg 69
31
Embodied Water, L/kg 190
65

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
140
Resilience: Unit (Modulus of Resilience), kJ/m3 140
920
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
23
Strength to Weight: Bending, points 20
21
Thermal Shock Resistance, points 13
20

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.13
Chromium (Cr), % 24 to 26
0 to 0.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 47.2 to 57
87.4 to 91.5
Manganese (Mn), % 0 to 2.0
0 to 0.9
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 19 to 22
8.5 to 10
Niobium (Nb), % 0 to 1.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.045
Vanadium (V), % 0
0 to 0.030