AISI 310Cb Stainless Steel vs. EN 1.4112 Stainless Steel

Both AISI 310Cb stainless steel and EN 1.4112 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 71% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310Cb stainless steel and the bottom bar is EN 1.4112 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
230
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
20
Fatigue Strength, MPa 200
280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 390
470
Tensile Strength: Ultimate (UTS), MPa 580
750
Tensile Strength: Yield (Proof), MPa 230
430

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 520
400
Maximum Temperature: Mechanical, °C 1100
910
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1360
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 28
10
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.8
2.6
Embodied Energy, MJ/kg 69
37
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 25
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
480
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
27
Strength to Weight: Bending, points 20
24
Thermal Diffusivity, mm2/s 3.9
4.1
Thermal Shock Resistance, points 13
26

Alloy Composition

Carbon (C), % 0 to 0.080
0.85 to 1.0
Chromium (Cr), % 24 to 26
17 to 19
Iron (Fe), % 47.2 to 57
76.6 to 81.2
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0.9 to 1.3
Nickel (Ni), % 19 to 22
0
Niobium (Nb), % 0 to 1.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 0
0.070 to 0.12