AISI 310Cb Stainless Steel vs. EN 1.4729 Stainless Steel

Both AISI 310Cb stainless steel and EN 1.4729 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 67% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AISI 310Cb stainless steel and the bottom bar is EN 1.4729 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
260
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
15
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
75

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 520
390
Maximum Temperature: Mechanical, °C 1100
850
Melting Completion (Liquidus), °C 1410
1420
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
24
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 28
7.5
Density, g/cm3 7.9
7.6
Embodied Carbon, kg CO2/kg material 4.8
2.1
Embodied Energy, MJ/kg 69
29
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 25
14
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Thermal Diffusivity, mm2/s 3.9
6.5

Alloy Composition

Carbon (C), % 0 to 0.080
0.3 to 0.5
Chromium (Cr), % 24 to 26
12 to 14
Iron (Fe), % 47.2 to 57
80.4 to 86.7
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 19 to 22
0 to 1.0
Niobium (Nb), % 0 to 1.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.5
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030