AISI 310Cb Stainless Steel vs. EN 1.4742 Stainless Steel

Both AISI 310Cb stainless steel and EN 1.4742 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 71% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310Cb stainless steel and the bottom bar is EN 1.4742 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
17
Fatigue Strength, MPa 200
180
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 390
370
Tensile Strength: Ultimate (UTS), MPa 580
600
Tensile Strength: Yield (Proof), MPa 230
300

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 520
410
Maximum Temperature: Mechanical, °C 1100
1000
Melting Completion (Liquidus), °C 1410
1420
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
19
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 28
9.0
Density, g/cm3 7.9
7.6
Embodied Carbon, kg CO2/kg material 4.8
2.2
Embodied Energy, MJ/kg 69
32
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 25
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
84
Resilience: Unit (Modulus of Resilience), kJ/m3 140
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 3.9
5.1
Thermal Shock Resistance, points 13
21

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.2
Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 24 to 26
17 to 19
Iron (Fe), % 47.2 to 57
77.2 to 81.6
Manganese (Mn), % 0 to 2.0
0 to 1.0
Nickel (Ni), % 19 to 22
0
Niobium (Nb), % 0 to 1.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.5
0.7 to 1.4
Sulfur (S), % 0 to 0.030
0 to 0.015