AISI 310Cb Stainless Steel vs. SAE-AISI 8115 Steel

Both AISI 310Cb stainless steel and SAE-AISI 8115 steel are iron alloys. They have 54% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310Cb stainless steel and the bottom bar is SAE-AISI 8115 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
15
Fatigue Strength, MPa 200
320
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 390
370
Tensile Strength: Ultimate (UTS), MPa 580
610
Tensile Strength: Yield (Proof), MPa 230
500

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
43
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.5
Embodied Energy, MJ/kg 69
19
Embodied Water, L/kg 190
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
86
Resilience: Unit (Modulus of Resilience), kJ/m3 140
660
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 3.9
12
Thermal Shock Resistance, points 13
19

Alloy Composition

Carbon (C), % 0 to 0.080
0.13 to 0.18
Chromium (Cr), % 24 to 26
0.3 to 0.5
Iron (Fe), % 47.2 to 57
97.4 to 98.4
Manganese (Mn), % 0 to 2.0
0.7 to 0.9
Molybdenum (Mo), % 0
0.080 to 0.15
Nickel (Ni), % 19 to 22
0.2 to 0.4
Niobium (Nb), % 0 to 1.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.5
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040