AISI 310Cb Stainless Steel vs. S21603 Stainless Steel

Both AISI 310Cb stainless steel and S21603 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 79% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310Cb stainless steel and the bottom bar is S21603 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
45
Fatigue Strength, MPa 200
360
Poisson's Ratio 0.28
0.28
Reduction in Area, % 46
57
Rockwell B Hardness 84
88
Shear Modulus, GPa 78
79
Shear Strength, MPa 390
490
Tensile Strength: Ultimate (UTS), MPa 580
690
Tensile Strength: Yield (Proof), MPa 230
390

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 520
420
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1410
1420
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Base Metal Price, % relative 28
17
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.8
3.6
Embodied Energy, MJ/kg 69
50
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 25
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
270
Resilience: Unit (Modulus of Resilience), kJ/m3 140
380
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 20
22
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 24 to 26
17.5 to 22
Iron (Fe), % 47.2 to 57
57.6 to 67.8
Manganese (Mn), % 0 to 2.0
7.5 to 9.0
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 19 to 22
5.0 to 7.0
Niobium (Nb), % 0 to 1.1
0
Nitrogen (N), % 0
0.25 to 0.5
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030