AISI 310HCb Stainless Steel vs. 85-silver 15-cadmium-oxide

AISI 310HCb stainless steel belongs to the iron alloys classification, while 85-silver 15-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.

For each property being compared, the top bar is AISI 310HCb stainless steel and the bottom bar is 85-silver 15-cadmium-oxide.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 7.9
10
Electrical Conductivity: Equal Volume, % IACS 2.1
64 to 82
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
57 to 73
Elongation at Break, % 46
2.2 to 16
Shear Strength, MPa 410
180 to 210
Strength to Weight: Axial, points 21
8.1 to 12
Strength to Weight: Bending, points 20
9.7 to 13
Tensile Strength: Ultimate (UTS), MPa 590
290 to 440