AISI 310MoLN Stainless Steel vs. ACI-ASTM CA6N Steel

Both AISI 310MoLN stainless steel and ACI-ASTM CA6N steel are iron alloys. They have 69% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ACI-ASTM CA6N steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
17
Fatigue Strength, MPa 210
640
Poisson's Ratio 0.28
0.28
Reduction in Area, % 45
57
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 610
1080
Tensile Strength: Yield (Proof), MPa 290
1060

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
390
Maximum Temperature: Mechanical, °C 1100
740
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
23
Thermal Expansion, µm/m-K 16
9.9

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 28
11
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
2.5
Embodied Energy, MJ/kg 70
35
Embodied Water, L/kg 200
110

Common Calculations

PREN (Pitting Resistance) 34
12
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
180
Resilience: Unit (Modulus of Resilience), kJ/m3 200
2900
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
38
Strength to Weight: Bending, points 20
30
Thermal Diffusivity, mm2/s 3.7
6.1
Thermal Shock Resistance, points 14
40

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.060
Chromium (Cr), % 24 to 26
10.5 to 12.5
Iron (Fe), % 45.2 to 53.8
77.9 to 83.5
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
6.0 to 8.0
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.020