AISI 310MoLN Stainless Steel vs. ACI-ASTM CH10 Steel

Both AISI 310MoLN stainless steel and ACI-ASTM CH10 steel are iron alloys. They have 88% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ACI-ASTM CH10 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
34
Fatigue Strength, MPa 210
180
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 610
540
Tensile Strength: Yield (Proof), MPa 290
230

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
440
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 28
20
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
3.7
Embodied Energy, MJ/kg 70
53
Embodied Water, L/kg 200
180

Common Calculations

PREN (Pitting Resistance) 34
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
150
Resilience: Unit (Modulus of Resilience), kJ/m3 200
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 3.7
3.9
Thermal Shock Resistance, points 14
12

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.1
Chromium (Cr), % 24 to 26
22 to 26
Iron (Fe), % 45.2 to 53.8
54.8 to 66
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 1.6 to 2.6
0 to 0.5
Nickel (Ni), % 20.5 to 23.5
12 to 15
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 2.0
Sulfur (S), % 0 to 0.010
0 to 0.040