AISI 310MoLN Stainless Steel vs. ASTM A148 Cast Steel

Both AISI 310MoLN stainless steel and ASTM A148 cast steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ASTM A148 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190 to 390
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
5.7 to 25
Fatigue Strength, MPa 210
280 to 670
Poisson's Ratio 0.28
0.29
Reduction in Area, % 45
13 to 45
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 610
630 to 1300
Tensile Strength: Yield (Proof), MPa 290
390 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400 to 430
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
37 to 47
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3 to 7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.3 to 8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.3 to 3.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
1.5 to 1.7
Embodied Energy, MJ/kg 70
20 to 22
Embodied Water, L/kg 200
48 to 53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
71 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 200
400 to 3570
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
22 to 46
Strength to Weight: Bending, points 20
21 to 34
Thermal Diffusivity, mm2/s 3.7
9.9 to 13
Thermal Shock Resistance, points 14
18 to 38