AISI 310MoLN Stainless Steel vs. ASTM A182 Grade F5a

Both AISI 310MoLN stainless steel and ASTM A182 grade F5a are iron alloys. They have 56% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ASTM A182 grade F5a.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
310
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
25
Fatigue Strength, MPa 210
380
Poisson's Ratio 0.28
0.29
Reduction in Area, % 45
56
Shear Modulus, GPa 80
74
Shear Strength, MPa 400
450
Tensile Strength: Ultimate (UTS), MPa 610
710
Tensile Strength: Yield (Proof), MPa 290
520

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
510
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 28
4.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
1.8
Embodied Energy, MJ/kg 70
24
Embodied Water, L/kg 200
69

Common Calculations

PREN (Pitting Resistance) 34
6.8
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
160
Resilience: Unit (Modulus of Resilience), kJ/m3 200
700
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
25
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.25
Chromium (Cr), % 24 to 26
4.0 to 6.0
Iron (Fe), % 45.2 to 53.8
91.4 to 95.6
Manganese (Mn), % 0 to 2.0
0 to 0.6
Molybdenum (Mo), % 1.6 to 2.6
0.44 to 0.65
Nickel (Ni), % 20.5 to 23.5
0 to 0.5
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030