AISI 310MoLN Stainless Steel vs. ASTM A231 Spring Steel

Both AISI 310MoLN stainless steel and ASTM A231 spring steel are iron alloys. They have 52% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ASTM A231 spring steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
540
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
14
Fatigue Strength, MPa 210
1000
Poisson's Ratio 0.28
0.29
Reduction in Area, % 45
46
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
1080
Tensile Strength: Ultimate (UTS), MPa 610
1790
Tensile Strength: Yield (Proof), MPa 290
1570

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
2.0
Embodied Energy, MJ/kg 70
28
Embodied Water, L/kg 200
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
230
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
64
Strength to Weight: Bending, points 20
42
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 14
53

Alloy Composition

Carbon (C), % 0 to 0.020
0.48 to 0.53
Chromium (Cr), % 24 to 26
0.8 to 1.1
Iron (Fe), % 45.2 to 53.8
96.7 to 97.7
Manganese (Mn), % 0 to 2.0
0.7 to 0.9
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
0
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.040
Vanadium (V), % 0
0.15 to 0.3