AISI 310MoLN Stainless Steel vs. ASTM A356 Grade 10

Both AISI 310MoLN stainless steel and ASTM A356 grade 10 are iron alloys. They have 54% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ASTM A356 grade 10.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
23
Fatigue Strength, MPa 210
300
Poisson's Ratio 0.28
0.29
Reduction in Area, % 45
39
Shear Modulus, GPa 80
74
Tensile Strength: Ultimate (UTS), MPa 610
670
Tensile Strength: Yield (Proof), MPa 290
430

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
460
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 28
3.9
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 5.0
1.8
Embodied Energy, MJ/kg 70
23
Embodied Water, L/kg 200
59

Common Calculations

PREN (Pitting Resistance) 34
5.9
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
130
Resilience: Unit (Modulus of Resilience), kJ/m3 200
480
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 14
19

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.2
Chromium (Cr), % 24 to 26
2.0 to 2.8
Iron (Fe), % 45.2 to 53.8
94.4 to 96.6
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 1.6 to 2.6
0.9 to 1.2
Nickel (Ni), % 20.5 to 23.5
0
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.030