AISI 310MoLN Stainless Steel vs. AWS E330

Both AISI 310MoLN stainless steel and AWS E330 are iron alloys. They have 85% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is AWS E330.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
29
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 610
580

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1380
1350
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
12
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 28
31
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 5.0
5.4
Embodied Energy, MJ/kg 70
75
Embodied Water, L/kg 200
180

Common Calculations

PREN (Pitting Resistance) 34
17
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
20
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 3.7
3.2
Thermal Shock Resistance, points 14
16

Alloy Composition

Carbon (C), % 0 to 0.020
0.18 to 0.25
Chromium (Cr), % 24 to 26
14 to 17
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 45.2 to 53.8
40.7 to 51.8
Manganese (Mn), % 0 to 2.0
1.0 to 2.5
Molybdenum (Mo), % 1.6 to 2.6
0 to 0.75
Nickel (Ni), % 20.5 to 23.5
33 to 37
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030