AISI 310MoLN Stainless Steel vs. EN 1.3536 Steel

Both AISI 310MoLN stainless steel and EN 1.3536 steel are iron alloys. They have 53% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 610
660

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
440
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
41
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
1.6
Embodied Energy, MJ/kg 70
21
Embodied Water, L/kg 200
55

Common Calculations

PREN (Pitting Resistance) 34
2.8
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
23
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 14
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.020
0.93 to 1.1
Chromium (Cr), % 24 to 26
1.7 to 2.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 45.2 to 53.8
96 to 97.4
Manganese (Mn), % 0 to 2.0
0.6 to 0.8
Molybdenum (Mo), % 1.6 to 2.6
0.2 to 0.35
Nickel (Ni), % 20.5 to 23.5
0
Nitrogen (N), % 0.090 to 0.15
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0.15 to 0.45
Sulfur (S), % 0 to 0.010
0 to 0.030