AISI 310MoLN Stainless Steel vs. EN 1.4306 Stainless Steel

Both AISI 310MoLN stainless steel and EN 1.4306 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is EN 1.4306 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
14 to 45
Fatigue Strength, MPa 210
190 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 400
400 to 550
Tensile Strength: Ultimate (UTS), MPa 610
580 to 900
Tensile Strength: Yield (Proof), MPa 290
210 to 570

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 28
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
3.2
Embodied Energy, MJ/kg 70
45
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 34
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 200
110 to 820
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
21 to 32
Strength to Weight: Bending, points 20
20 to 27
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 14
13 to 20

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.030
Chromium (Cr), % 24 to 26
18 to 20
Iron (Fe), % 45.2 to 53.8
64.8 to 72
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
10 to 12
Nitrogen (N), % 0.090 to 0.15
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015