AISI 310MoLN Stainless Steel vs. EN 1.4517 Stainless Steel

Both AISI 310MoLN stainless steel and EN 1.4517 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is EN 1.4517 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
25
Fatigue Strength, MPa 210
380
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
79
Tensile Strength: Ultimate (UTS), MPa 610
730
Tensile Strength: Yield (Proof), MPa 290
550

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1380
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
17
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 28
20
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
3.8
Embodied Energy, MJ/kg 70
53
Embodied Water, L/kg 200
180

Common Calculations

PREN (Pitting Resistance) 34
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
170
Resilience: Unit (Modulus of Resilience), kJ/m3 200
740
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
26
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 3.7
4.6
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.030
Chromium (Cr), % 24 to 26
24.5 to 26.5
Copper (Cu), % 0
2.8 to 3.5
Iron (Fe), % 45.2 to 53.8
56.7 to 65.1
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 1.6 to 2.6
2.5 to 3.5
Nickel (Ni), % 20.5 to 23.5
5.0 to 7.0
Nitrogen (N), % 0.090 to 0.15
0.12 to 0.22
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.025