AISI 310MoLN Stainless Steel vs. EN 1.4537 Stainless Steel

Both AISI 310MoLN stainless steel and EN 1.4537 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is EN 1.4537 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
220
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 28
42
Fatigue Strength, MPa 210
290
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
80
Shear Strength, MPa 400
480
Tensile Strength: Ultimate (UTS), MPa 610
700
Tensile Strength: Yield (Proof), MPa 290
330

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1390
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 28
34
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 5.0
6.1
Embodied Energy, MJ/kg 70
84
Embodied Water, L/kg 200
220

Common Calculations

PREN (Pitting Resistance) 34
46
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
240
Resilience: Unit (Modulus of Resilience), kJ/m3 200
270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 3.7
3.7
Thermal Shock Resistance, points 14
15

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.020
Chromium (Cr), % 24 to 26
24 to 26
Copper (Cu), % 0
1.0 to 2.0
Iron (Fe), % 45.2 to 53.8
36.3 to 46.1
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 1.6 to 2.6
4.7 to 5.7
Nickel (Ni), % 20.5 to 23.5
24 to 27
Nitrogen (N), % 0.090 to 0.15
0.17 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.7
Sulfur (S), % 0 to 0.010
0 to 0.010