AISI 310MoLN Stainless Steel vs. EN 1.7077 Steel

Both AISI 310MoLN stainless steel and EN 1.7077 steel are iron alloys. They have 52% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is EN 1.7077 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Reduction in Area, % 45
63 to 68
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 610
490 to 1750

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
45
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
1.4
Embodied Energy, MJ/kg 70
19
Embodied Water, L/kg 200
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17 to 62
Strength to Weight: Bending, points 20
18 to 41
Thermal Diffusivity, mm2/s 3.7
12
Thermal Shock Resistance, points 14
14 to 51

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.020
0.34 to 0.38
Chromium (Cr), % 24 to 26
0.9 to 1.2
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 45.2 to 53.8
96.8 to 98.1
Manganese (Mn), % 0 to 2.0
0.7 to 1.0
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
0
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.025