AISI 310MoLN Stainless Steel vs. EN 1.8062 Steel

Both AISI 310MoLN stainless steel and EN 1.8062 steel are iron alloys. They have 51% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is EN 1.8062 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200 to 510
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
72
Tensile Strength: Ultimate (UTS), MPa 610
660 to 1910

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
43
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.4
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 5.0
1.5
Embodied Energy, MJ/kg 70
20
Embodied Water, L/kg 200
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
24 to 69
Strength to Weight: Bending, points 20
22 to 44
Thermal Diffusivity, mm2/s 3.7
12
Thermal Shock Resistance, points 14
20 to 57

Alloy Composition

Carbon (C), % 0 to 0.020
0.42 to 0.5
Chromium (Cr), % 24 to 26
0.5 to 0.8
Iron (Fe), % 45.2 to 53.8
95.9 to 97.1
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 1.6 to 2.6
0.2 to 0.3
Nickel (Ni), % 20.5 to 23.5
0
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
1.3 to 1.7
Sulfur (S), % 0 to 0.010
0 to 0.025