AISI 310MoLN Stainless Steel vs. EN 1.8932 Steel

Both AISI 310MoLN stainless steel and EN 1.8932 steel are iron alloys. They have 51% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is EN 1.8932 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
20
Fatigue Strength, MPa 210
250
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
370
Tensile Strength: Ultimate (UTS), MPa 610
600
Tensile Strength: Yield (Proof), MPa 290
370

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
1.7
Embodied Energy, MJ/kg 70
24
Embodied Water, L/kg 200
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
100
Resilience: Unit (Modulus of Resilience), kJ/m3 200
370
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 14
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Carbon (C), % 0 to 0.020
0 to 0.2
Chromium (Cr), % 24 to 26
0 to 0.3
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 45.2 to 53.8
95.5 to 98.9
Manganese (Mn), % 0 to 2.0
1.0 to 1.7
Molybdenum (Mo), % 1.6 to 2.6
0 to 0.1
Nickel (Ni), % 20.5 to 23.5
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.090 to 0.15
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0.1 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.015
Vanadium (V), % 0
0 to 0.2