AISI 310MoLN Stainless Steel vs. SAE-AISI 1026 Steel

Both AISI 310MoLN stainless steel and SAE-AISI 1026 steel are iron alloys. They have 50% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is SAE-AISI 1026 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140 to 160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
17 to 27
Fatigue Strength, MPa 210
200 to 310
Poisson's Ratio 0.28
0.29
Reduction in Area, % 45
45 to 55
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
320 to 340
Tensile Strength: Ultimate (UTS), MPa 610
500 to 550
Tensile Strength: Yield (Proof), MPa 290
270 to 470

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
52
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 28
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 5.0
1.4
Embodied Energy, MJ/kg 70
18
Embodied Water, L/kg 200
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
89 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 200
200 to 580
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
18 to 20
Strength to Weight: Bending, points 20
18 to 19
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 14
16 to 18

Alloy Composition

Carbon (C), % 0 to 0.020
0.22 to 0.28
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 45.2 to 53.8
98.7 to 99.18
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
0
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0 to 0.050