AISI 310MoLN Stainless Steel vs. S44330 Stainless Steel

Both AISI 310MoLN stainless steel and S44330 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 72% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is S44330 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
25
Fatigue Strength, MPa 210
160
Poisson's Ratio 0.28
0.27
Rockwell B Hardness 84
79
Shear Modulus, GPa 80
78
Shear Strength, MPa 400
280
Tensile Strength: Ultimate (UTS), MPa 610
440
Tensile Strength: Yield (Proof), MPa 290
230

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 450
560
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
21
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 28
13
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 5.0
2.8
Embodied Energy, MJ/kg 70
40
Embodied Water, L/kg 200
140

Common Calculations

PREN (Pitting Resistance) 34
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
91
Resilience: Unit (Modulus of Resilience), kJ/m3 200
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
16
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 3.7
5.7
Thermal Shock Resistance, points 14
16

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.025
Chromium (Cr), % 24 to 26
20 to 23
Copper (Cu), % 0
0.3 to 0.8
Iron (Fe), % 45.2 to 53.8
72.5 to 79.7
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
0
Niobium (Nb), % 0
0 to 0.8
Nitrogen (N), % 0.090 to 0.15
0 to 0.025
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0
0 to 0.8