AISI 310S stainless steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is 92-silver 8-tin-oxide.

Metric UnitsUS Customary Units

Material Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
76 to 80
Elongation at Break, % 34 to 44
32 to 34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
62 to 110
Shear Strength, MPa 420 to 470
150 to 210
Tensile Strength: Ultimate (UTS), MPa 600 to 710
230 to 320
Tensile Strength: Yield (Proof), MPa 270 to 350
120 to 300