AISI 310S Stainless Steel vs. AWS BAg-22

AISI 310S stainless steel belongs to the iron alloys classification, while AWS BAg-22 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is AWS BAg-22.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
96
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 79
36
Tensile Strength: Ultimate (UTS), MPa 600 to 710
140

Thermal Properties

Latent Heat of Fusion, J/g 310
150
Melting Completion (Liquidus), °C 1450
700
Melting Onset (Solidus), °C 1400
680
Specific Heat Capacity, J/kg-K 480
320
Thermal Expansion, µm/m-K 16
21

Otherwise Unclassified Properties

Density, g/cm3 7.9
9.0
Embodied Carbon, kg CO2/kg material 4.3
48
Embodied Energy, MJ/kg 61
760

Common Calculations

Stiffness to Weight: Axial, points 14
5.9
Stiffness to Weight: Bending, points 25
17
Strength to Weight: Axial, points 21 to 25
4.3
Strength to Weight: Bending, points 20 to 22
6.6
Thermal Shock Resistance, points 14 to 16
5.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
15 to 17
Iron (Fe), % 48.3 to 57
0
Manganese (Mn), % 0 to 2.0
7.0 to 8.0
Nickel (Ni), % 19 to 22
4.0 to 5.0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0
Silver (Ag), % 0
48 to 50
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
21 to 25
Residuals, % 0
0 to 0.15