AISI 310S Stainless Steel vs. AWS BAu-1

AISI 310S stainless steel belongs to the iron alloys classification, while AWS BAu-1 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is AWS BAu-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Poisson's Ratio 0.27
0.37
Shear Modulus, GPa 79
40
Tensile Strength: Ultimate (UTS), MPa 600 to 710
210

Thermal Properties

Latent Heat of Fusion, J/g 310
150
Melting Completion (Liquidus), °C 1450
1020
Melting Onset (Solidus), °C 1400
990
Specific Heat Capacity, J/kg-K 480
290
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Density, g/cm3 7.9
13

Common Calculations

Stiffness to Weight: Axial, points 14
4.7
Stiffness to Weight: Bending, points 25
12
Strength to Weight: Axial, points 21 to 25
4.5
Strength to Weight: Bending, points 20 to 22
6.1
Thermal Shock Resistance, points 14 to 16
8.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
61.9 to 63
Gold (Au), % 0
37 to 38
Iron (Fe), % 48.3 to 57
0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.030
0
Residuals, % 0
0 to 0.15