AISI 310S Stainless Steel vs. AWS BVAg-29

AISI 310S stainless steel belongs to the iron alloys classification, while AWS BVAg-29 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is AWS BVAg-29.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
73
Poisson's Ratio 0.27
0.37
Shear Modulus, GPa 79
27
Tensile Strength: Ultimate (UTS), MPa 600 to 710
180

Thermal Properties

Latent Heat of Fusion, J/g 310
120
Melting Completion (Liquidus), °C 1450
710
Melting Onset (Solidus), °C 1400
620
Specific Heat Capacity, J/kg-K 480
270
Thermal Expansion, µm/m-K 16
20

Otherwise Unclassified Properties

Density, g/cm3 7.9
9.7

Common Calculations

Stiffness to Weight: Axial, points 14
4.2
Stiffness to Weight: Bending, points 25
14
Strength to Weight: Axial, points 21 to 25
5.2
Strength to Weight: Bending, points 20 to 22
7.3
Thermal Shock Resistance, points 14 to 16
8.8

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.080
0 to 0.0050
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
22.5 to 25.5
Indium (In), % 0
14 to 15
Iron (Fe), % 48.3 to 57
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.045
0 to 0.0020
Silicon (Si), % 0 to 1.5
0
Silver (Ag), % 0
60.5 to 62.5
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
0 to 0.0010