AISI 310S Stainless Steel vs. AWS E430Nb

Both AISI 310S stainless steel and AWS E430Nb are iron alloys. They have 71% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is AWS E430Nb.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34 to 44
23
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 600 to 710
500

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
24
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 25
15
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
3.1
Embodied Energy, MJ/kg 61
45
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 25
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 25
18
Strength to Weight: Bending, points 20 to 22
18
Thermal Diffusivity, mm2/s 4.1
6.6
Thermal Shock Resistance, points 14 to 16
13

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.1
Chromium (Cr), % 24 to 26
15 to 18
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 48.3 to 57
76.2 to 84.5
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 19 to 22
0 to 0.6
Niobium (Nb), % 0
0.5 to 1.5
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030