MakeItFrom.com
Menu (ESC)

AISI 310S Stainless Steel vs. EN 1.4409 Stainless Steel

Both AISI 310S stainless steel and EN 1.4409 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is EN 1.4409 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 210
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34 to 44
34
Fatigue Strength, MPa 250 to 280
180
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 600 to 710
490
Tensile Strength: Yield (Proof), MPa 270 to 350
220

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
19
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
3.7
Embodied Energy, MJ/kg 61
52
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 25
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
140
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
120
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 25
17
Strength to Weight: Bending, points 20 to 22
18
Thermal Diffusivity, mm2/s 4.1
4.1
Thermal Shock Resistance, points 14 to 16
11

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 24 to 26
18 to 20
Iron (Fe), % 48.3 to 57
61.7 to 71
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 19 to 22
9.0 to 12
Nitrogen (N), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.5
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.025