AISI 310S Stainless Steel vs. EN 1.5522 Steel

Both AISI 310S stainless steel and EN 1.5522 steel are iron alloys. They have 54% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is EN 1.5522 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 210
140 to 190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34 to 44
11 to 21
Fatigue Strength, MPa 250 to 280
210 to 330
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 420 to 470
320 to 380
Tensile Strength: Ultimate (UTS), MPa 600 to 710
450 to 1490
Tensile Strength: Yield (Proof), MPa 270 to 350
300 to 520

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 25
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.4
Embodied Energy, MJ/kg 61
19
Embodied Water, L/kg 190
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
45 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
250 to 720
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 25
16 to 53
Strength to Weight: Bending, points 20 to 22
17 to 37
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 14 to 16
13 to 44

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.080
0.2 to 0.24
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 48.3 to 57
98 to 98.9
Manganese (Mn), % 0 to 2.0
0.9 to 1.2
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.5
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025

Comparable Variants