AISI 310S Stainless Steel vs. EN 2.4654 Nickel

AISI 310S stainless steel belongs to the iron alloys classification, while EN 2.4654 nickel belongs to the nickel alloys. They have 42% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is EN 2.4654 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34 to 44
17
Fatigue Strength, MPa 250 to 280
460
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
77
Shear Strength, MPa 420 to 470
770
Tensile Strength: Ultimate (UTS), MPa 600 to 710
1250
Tensile Strength: Yield (Proof), MPa 270 to 350
850

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Mechanical, °C 1100
1000
Melting Completion (Liquidus), °C 1450
1390
Melting Onset (Solidus), °C 1400
1330
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 16
13
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 25
75
Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 4.3
10
Embodied Energy, MJ/kg 61
150
Embodied Water, L/kg 190
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
190
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
1810
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 21 to 25
42
Strength to Weight: Bending, points 20 to 22
31
Thermal Diffusivity, mm2/s 4.1
3.3
Thermal Shock Resistance, points 14 to 16
37

Alloy Composition

Aluminum (Al), % 0
1.2 to 1.6
Boron (B), % 0
0.0030 to 0.010
Carbon (C), % 0 to 0.080
0.020 to 0.1
Chromium (Cr), % 24 to 26
18 to 21
Cobalt (Co), % 0
12 to 15
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 48.3 to 57
0 to 2.0
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
3.5 to 5.0
Nickel (Ni), % 19 to 22
50.6 to 62.5
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 0 to 1.5
0 to 0.15
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
2.8 to 3.3
Zirconium (Zr), % 0
0.020 to 0.080