AISI 310S Stainless Steel vs. CC498K Bronze

AISI 310S stainless steel belongs to the iron alloys classification, while CC498K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is CC498K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 210
78
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34 to 44
14
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 79
41
Tensile Strength: Ultimate (UTS), MPa 600 to 710
260
Tensile Strength: Yield (Proof), MPa 270 to 350
130

Thermal Properties

Latent Heat of Fusion, J/g 310
190
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1450
1000
Melting Onset (Solidus), °C 1400
920
Specific Heat Capacity, J/kg-K 480
370
Thermal Conductivity, W/m-K 16
73
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
10
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
10

Otherwise Unclassified Properties

Base Metal Price, % relative 25
32
Density, g/cm3 7.9
8.8
Embodied Carbon, kg CO2/kg material 4.3
3.2
Embodied Energy, MJ/kg 61
52
Embodied Water, L/kg 190
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
30
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
72
Stiffness to Weight: Axial, points 14
6.9
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21 to 25
8.1
Strength to Weight: Bending, points 20 to 22
10
Thermal Diffusivity, mm2/s 4.1
22
Thermal Shock Resistance, points 14 to 16
9.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
85 to 90
Iron (Fe), % 48.3 to 57
0 to 0.25
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0 to 1.0
Phosphorus (P), % 0 to 0.045
0 to 0.050
Silicon (Si), % 0 to 1.5
0 to 0.010
Sulfur (S), % 0 to 0.030
0 to 0.1
Tin (Sn), % 0
5.5 to 6.5
Zinc (Zn), % 0
3.0 to 5.0