AISI 310S Stainless Steel vs. Solder Alloy 801

AISI 310S stainless steel belongs to the iron alloys classification, while solder alloy 801 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is solder alloy 801.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 210
22
Elastic (Young's, Tensile) Modulus, GPa 200
53
Elongation at Break, % 34 to 44
33
Poisson's Ratio 0.27
0.35
Shear Modulus, GPa 79
20
Tensile Strength: Ultimate (UTS), MPa 600 to 710
55

Thermal Properties

Latent Heat of Fusion, J/g 310
64
Melting Completion (Liquidus), °C 1450
200
Melting Onset (Solidus), °C 1400
200
Specific Heat Capacity, J/kg-K 480
240
Thermal Conductivity, W/m-K 16
61
Thermal Expansion, µm/m-K 16
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
15
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
19

Otherwise Unclassified Properties

Density, g/cm3 7.9
7.2
Embodied Carbon, kg CO2/kg material 4.3
14
Embodied Energy, MJ/kg 61
240
Embodied Water, L/kg 190
1140

Common Calculations

Stiffness to Weight: Axial, points 14
4.1
Stiffness to Weight: Bending, points 25
17
Strength to Weight: Axial, points 21 to 25
2.1
Strength to Weight: Bending, points 20 to 22
4.4
Thermal Diffusivity, mm2/s 4.1
36
Thermal Shock Resistance, points 14 to 16
3.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 48.3 to 57
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0 to 0.010
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
89.9 to 91.5
Zinc (Zn), % 0
8.5 to 9.5