AISI 310S Stainless Steel vs. Nickel 825

AISI 310S stainless steel belongs to the iron alloys classification, while nickel 825 belongs to the nickel alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is nickel 825.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34 to 44
34
Fatigue Strength, MPa 250 to 280
190
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
78
Shear Strength, MPa 420 to 470
430
Tensile Strength: Ultimate (UTS), MPa 600 to 710
650
Tensile Strength: Yield (Proof), MPa 270 to 350
260

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Mechanical, °C 1100
980
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 16
11
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.7

Otherwise Unclassified Properties

Base Metal Price, % relative 25
41
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.3
7.2
Embodied Energy, MJ/kg 61
100
Embodied Water, L/kg 190
230

Common Calculations

PREN (Pitting Resistance) 25
31
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
180
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 25
22
Strength to Weight: Bending, points 20 to 22
20
Thermal Diffusivity, mm2/s 4.1
2.9
Thermal Shock Resistance, points 14 to 16
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.2
Carbon (C), % 0 to 0.080
0 to 0.050
Chromium (Cr), % 24 to 26
19.5 to 23.5
Copper (Cu), % 0
1.5 to 3.0
Iron (Fe), % 48.3 to 57
22 to 37.9
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 19 to 22
38 to 46
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0 to 0.050
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0.6 to 1.2