MakeItFrom.com
Menu (ESC)

AISI 310S Stainless Steel vs. SAE-AISI H11 Steel

Both AISI 310S stainless steel and SAE-AISI H11 steel are iron alloys. They have 59% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is SAE-AISI H11 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
74
Tensile Strength: Ultimate (UTS), MPa 600 to 710
690 to 1840

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
42
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
5.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
3.0
Embodied Energy, MJ/kg 61
43
Embodied Water, L/kg 190
75

Common Calculations

PREN (Pitting Resistance) 25
9.6
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 25
25 to 66
Strength to Weight: Bending, points 20 to 22
22 to 43
Thermal Diffusivity, mm2/s 4.1
11
Thermal Shock Resistance, points 14 to 16
22 to 58

Alloy Composition

Carbon (C), % 0 to 0.080
0.33 to 0.43
Chromium (Cr), % 24 to 26
4.8 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 48.3 to 57
89.6 to 92.5
Manganese (Mn), % 0 to 2.0
0.2 to 0.5
Molybdenum (Mo), % 0
1.1 to 1.6
Nickel (Ni), % 19 to 22
0 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.5
0.8 to 1.2
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0.3 to 0.6