AISI 310S Stainless Steel vs. SAE-AISI M43 Steel

Both AISI 310S stainless steel and SAE-AISI M43 steel are iron alloys. They have 57% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is SAE-AISI M43 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 600 to 710
810 to 2290

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1450
1550
Melting Onset (Solidus), °C 1400
1500
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 16
19
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 25
33
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.3
8.5
Embodied Energy, MJ/kg 61
120
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 25
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 25
27 to 77
Strength to Weight: Bending, points 20 to 22
24 to 47
Thermal Diffusivity, mm2/s 4.1
5.3
Thermal Shock Resistance, points 14 to 16
25 to 71

Alloy Composition

Carbon (C), % 0 to 0.080
1.2 to 1.3
Chromium (Cr), % 24 to 26
3.5 to 4.3
Cobalt (Co), % 0
7.8 to 8.8
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 48.3 to 57
70.8 to 76
Manganese (Mn), % 0 to 2.0
0.2 to 0.4
Molybdenum (Mo), % 0
7.5 to 8.5
Nickel (Ni), % 19 to 22
0 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.5
0.15 to 0.65
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
2.3 to 3.0
Vanadium (V), % 0
1.5 to 1.8