AISI 310S Stainless Steel vs. C47940 Brass

AISI 310S stainless steel belongs to the iron alloys classification, while C47940 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is C47940 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 34 to 44
14 to 34
Poisson's Ratio 0.27
0.31
Shear Modulus, GPa 79
40
Shear Strength, MPa 420 to 470
250 to 310
Tensile Strength: Ultimate (UTS), MPa 600 to 710
380 to 520
Tensile Strength: Yield (Proof), MPa 270 to 350
160 to 390

Thermal Properties

Latent Heat of Fusion, J/g 310
170
Maximum Temperature: Mechanical, °C 1100
130
Melting Completion (Liquidus), °C 1450
850
Melting Onset (Solidus), °C 1400
800
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 16
110
Thermal Expansion, µm/m-K 16
20

Otherwise Unclassified Properties

Base Metal Price, % relative 25
25
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.3
2.8
Embodied Energy, MJ/kg 61
47
Embodied Water, L/kg 190
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
68 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
120 to 740
Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21 to 25
13 to 17
Strength to Weight: Bending, points 20 to 22
14 to 17
Thermal Diffusivity, mm2/s 4.1
36
Thermal Shock Resistance, points 14 to 16
13 to 17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
63 to 66
Iron (Fe), % 48.3 to 57
0.1 to 1.0
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0.1 to 0.5
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
1.2 to 2.0
Zinc (Zn), % 0
28.1 to 34.6
Residuals, % 0
0 to 0.4