AISI 310S Stainless Steel vs. C74400 Nickel Silver

AISI 310S stainless steel belongs to the iron alloys classification, while C74400 nickel silver belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is C74400 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34 to 44
43
Poisson's Ratio 0.27
0.31
Shear Modulus, GPa 79
39
Shear Strength, MPa 420 to 470
240
Tensile Strength: Ultimate (UTS), MPa 600 to 710
350
Tensile Strength: Yield (Proof), MPa 270 to 350
120

Thermal Properties

Latent Heat of Fusion, J/g 310
180
Maximum Temperature: Mechanical, °C 1100
140
Melting Completion (Liquidus), °C 1450
930
Melting Onset (Solidus), °C 1400
910
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 16
120
Thermal Expansion, µm/m-K 16
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
26
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
29

Otherwise Unclassified Properties

Base Metal Price, % relative 25
25
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.3
2.9
Embodied Energy, MJ/kg 61
48
Embodied Water, L/kg 190
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
120
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
63
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21 to 25
12
Strength to Weight: Bending, points 20 to 22
14
Thermal Diffusivity, mm2/s 4.1
37
Thermal Shock Resistance, points 14 to 16
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
62 to 66
Iron (Fe), % 48.3 to 57
0 to 0.050
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
2.0 to 4.0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
29.6 to 36
Residuals, % 0
0 to 0.3