AISI 310S Stainless Steel vs. C99600 Bronze
AISI 310S stainless steel belongs to the iron alloys classification, while C99600 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is C99600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 150 |
| Elongation at Break, % | 34 to 44 | |
| 27 to 34 |
| Poisson's Ratio | 0.27 | |
| 0.34 |
| Shear Modulus, GPa | 79 | |
| 56 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 710 | |
| 560 |
| Tensile Strength: Yield (Proof), MPa | 270 to 350 | |
| 250 to 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 200 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1100 |
| Melting Onset (Solidus), °C | 1400 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Expansion, µm/m-K | 16 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 22 |
| Density, g/cm3 | 7.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 4.3 | |
| 3.2 |
| Embodied Energy, MJ/kg | 61 | |
| 51 |
| Embodied Water, L/kg | 190 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 220 | |
| 130 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 310 | |
| 210 to 310 |
| Stiffness to Weight: Axial, points | 14 | |
| 10 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 19 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 19 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 1.0 to 2.8 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.050 |
| Chromium (Cr), % | 24 to 26 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 | |
| 50.8 to 60 |
| Iron (Fe), % | 48.3 to 57 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 2.0 | |
| 39 to 45 |
| Nickel (Ni), % | 19 to 22 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.5 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.3 |