AISI 310S Stainless Steel vs. N10276 Nickel

AISI 310S stainless steel belongs to the iron alloys classification, while N10276 nickel belongs to the nickel alloys. They have 42% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is N10276 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Elongation at Break, % 34 to 44
47
Fatigue Strength, MPa 250 to 280
280
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
84
Shear Strength, MPa 420 to 470
550
Tensile Strength: Ultimate (UTS), MPa 600 to 710
780
Tensile Strength: Yield (Proof), MPa 270 to 350
320

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1450
1370
Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 16
9.1
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
70
Density, g/cm3 7.9
9.1
Embodied Carbon, kg CO2/kg material 4.3
13
Embodied Energy, MJ/kg 61
170
Embodied Water, L/kg 190
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
300
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
230
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 21 to 25
24
Strength to Weight: Bending, points 20 to 22
21
Thermal Diffusivity, mm2/s 4.1
2.4
Thermal Shock Resistance, points 14 to 16
23

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.010
Chromium (Cr), % 24 to 26
14.5 to 16.5
Cobalt (Co), % 0
0 to 2.5
Iron (Fe), % 48.3 to 57
4.0 to 7.0
Manganese (Mn), % 0 to 2.0
0 to 0.010
Molybdenum (Mo), % 0
15 to 17
Nickel (Ni), % 19 to 22
51 to 63.5
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 0.080
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
3.0 to 4.5
Vanadium (V), % 0
0 to 0.35