MakeItFrom.com
Menu (ESC)

AISI 310S Stainless Steel vs. R30001 Cobalt

AISI 310S stainless steel belongs to the iron alloys classification, while R30001 cobalt belongs to the cobalt alloys. They have a modest 29% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is R30001 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Elongation at Break, % 34 to 44
1.0
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
86
Tensile Strength: Ultimate (UTS), MPa 600 to 710
620

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Melting Completion (Liquidus), °C 1450
1530
Melting Onset (Solidus), °C 1400
1260
Specific Heat Capacity, J/kg-K 480
430
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.8

Otherwise Unclassified Properties

Density, g/cm3 7.9
9.0
Embodied Carbon, kg CO2/kg material 4.3
8.9
Embodied Energy, MJ/kg 61
130
Embodied Water, L/kg 190
460

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 21 to 25
19
Strength to Weight: Bending, points 20 to 22
18
Thermal Diffusivity, mm2/s 4.1
3.7
Thermal Shock Resistance, points 14 to 16
19

Alloy Composition

Carbon (C), % 0 to 0.080
2.0 to 3.0
Chromium (Cr), % 24 to 26
28 to 32
Cobalt (Co), % 0
43 to 59
Iron (Fe), % 48.3 to 57
0 to 3.0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 19 to 22
0 to 3.0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0 to 2.0
Sulfur (S), % 0 to 0.030
0
Tungsten (W), % 0
11 to 13