AISI 312 Stainless Steel vs. EN 1.5535 Steel

Both AISI 312 stainless steel and EN 1.5535 steel are iron alloys. They have 67% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 312 stainless steel and the bottom bar is EN 1.5535 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
11 to 22
Fatigue Strength, MPa 370
210 to 320
Poisson's Ratio 0.27
0.29
Reduction in Area, % 56
62 to 72
Shear Modulus, GPa 80
73
Shear Strength, MPa 510
320 to 370
Tensile Strength: Ultimate (UTS), MPa 780
450 to 1490
Tensile Strength: Yield (Proof), MPa 510
300 to 500

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
50
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 17
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.4
Embodied Energy, MJ/kg 48
19
Embodied Water, L/kg 170
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
45 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 640
240 to 680
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
16 to 53
Strength to Weight: Bending, points 24
17 to 37
Thermal Diffusivity, mm2/s 4.3
13
Thermal Shock Resistance, points 21
13 to 44

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.030
0.2 to 0.25
Chromium (Cr), % 24 to 26
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 62.2 to 69.2
97.6 to 98.9
Manganese (Mn), % 0 to 2.0
0.9 to 1.2
Molybdenum (Mo), % 1.2 to 2.0
0
Nickel (Ni), % 5.5 to 6.5
0
Nitrogen (N), % 0.14 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025