AISI 316H Stainless Steel vs. AWS ER100S-1
Both AISI 316H stainless steel and AWS ER100S-1 are iron alloys. They have 71% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AISI 316H stainless steel and the bottom bar is AWS ER100S-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 40 | |
| 18 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 49 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 3.6 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 1.8 |
| Embodied Energy, MJ/kg | 53 | |
| 24 |
| Embodied Water, L/kg | 150 | |
| 54 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 1290 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 21 | |
| 27 |
| Strength to Weight: Bending, points | 20 | |
| 24 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 13 |
| Thermal Shock Resistance, points | 13 | |
| 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 0 to 0.1 |
| Carbon (C), % | 0.040 to 0.1 | |
| 0 to 0.080 |
| Chromium (Cr), % | 16 to 18 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 62.1 to 72 | |
| 93.5 to 96.9 |
| Manganese (Mn), % | 0 to 2.0 | |
| 1.3 to 1.8 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0.25 to 0.55 |
| Nickel (Ni), % | 10 to 14 | |
| 1.4 to 2.1 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.75 | |
| 0.2 to 0.55 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |