AISI 316L Stainless Steel vs. EN 1.1152 Steel

Both AISI 316L stainless steel and EN 1.1152 steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 316L stainless steel and the bottom bar is EN 1.1152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 350
120 to 160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 9.0 to 50
12 to 22
Fatigue Strength, MPa 170 to 450
190 to 300
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 370 to 690
290 to 340
Tensile Strength: Ultimate (UTS), MPa 530 to 1160
400 to 550
Tensile Strength: Yield (Proof), MPa 190 to 870
270 to 440

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 870
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.9
1.4
Embodied Energy, MJ/kg 53
18
Embodied Water, L/kg 150
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 77 to 230
41 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 93 to 1880
200 to 530
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
14 to 19
Strength to Weight: Bending, points 18 to 31
15 to 19
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 12 to 25
13 to 17

Alloy Composition

Carbon (C), % 0 to 0.030
0.18 to 0.22
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 62 to 72
98.6 to 99.52
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 10 to 14
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025

Comparable Variants