AISI 316N Stainless Steel vs. Monel K-500

AISI 316N stainless steel belongs to the iron alloys classification, while Monel K-500 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 316N stainless steel and the bottom bar is Monel K-500.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
160
Elongation at Break, % 9.0 to 39
25 to 36
Fatigue Strength, MPa 230 to 450
260 to 560
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 78
61
Shear Strength, MPa 420 to 690
430 to 700
Tensile Strength: Ultimate (UTS), MPa 620 to 1160
640 to 1100
Tensile Strength: Yield (Proof), MPa 270 to 870
310 to 880

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Mechanical, °C 940
900
Melting Completion (Liquidus), °C 1440
1350
Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 15
18
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
3.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
50
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 3.9
8.1
Embodied Energy, MJ/kg 53
120
Embodied Water, L/kg 150
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95 to 230
180 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 1880
300 to 2420
Stiffness to Weight: Axial, points 14
10
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 22 to 41
21 to 35
Strength to Weight: Bending, points 20 to 31
19 to 27
Thermal Diffusivity, mm2/s 4.1
4.8
Thermal Shock Resistance, points 14 to 26
21 to 36

Alloy Composition

Aluminum (Al), % 0
2.3 to 3.2
Carbon (C), % 0 to 0.080
0 to 0.18
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
27 to 33
Iron (Fe), % 61.9 to 71.9
0 to 2.0
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 10 to 14
63 to 70.4
Nitrogen (N), % 0.1 to 0.16
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.35 to 0.85

Comparable Variants