AISI 317 Stainless Steel vs. EN 1.7383 Steel

Both AISI 317 stainless steel and EN 1.7383 steel are iron alloys. They have 67% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 317 stainless steel and the bottom bar is EN 1.7383 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 220
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 35 to 55
20 to 23
Fatigue Strength, MPa 250 to 330
210 to 270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
74
Shear Strength, MPa 420 to 470
350 to 380
Tensile Strength: Ultimate (UTS), MPa 580 to 710
560 to 610
Tensile Strength: Yield (Proof), MPa 250 to 420
300 to 400

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 590
460
Melting Completion (Liquidus), °C 1400
1470
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 21
3.9
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.3
1.8
Embodied Energy, MJ/kg 59
23
Embodied Water, L/kg 160
59

Common Calculations

PREN (Pitting Resistance) 31
5.6
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210 to 260
110
Resilience: Unit (Modulus of Resilience), kJ/m3 150 to 430
240 to 420
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20 to 25
20 to 22
Strength to Weight: Bending, points 20 to 22
19 to 20
Thermal Diffusivity, mm2/s 4.1
11
Thermal Shock Resistance, points 12 to 15
16 to 18

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0 to 0.080
0.080 to 0.15
Chromium (Cr), % 18 to 20
2.0 to 2.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 58 to 68
94.3 to 96.6
Manganese (Mn), % 0 to 2.0
0.4 to 0.8
Molybdenum (Mo), % 3.0 to 4.0
0.9 to 1.1
Nickel (Ni), % 11 to 15
0 to 0.3
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010