AISI 410Cb Stainless Steel vs. EN 1.6368 Steel

Both AISI 410Cb stainless steel and EN 1.6368 steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 410Cb stainless steel and the bottom bar is EN 1.6368 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 270
200 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 15
18
Fatigue Strength, MPa 180 to 460
310 to 330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 340 to 590
410 to 430
Tensile Strength: Ultimate (UTS), MPa 550 to 960
660 to 690
Tensile Strength: Yield (Proof), MPa 310 to 790
460 to 490

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 730
410
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
3.4
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.0
1.7
Embodied Energy, MJ/kg 29
22
Embodied Water, L/kg 97
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70 to 130
110
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 1600
580 to 650
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20 to 35
23 to 24
Strength to Weight: Bending, points 19 to 28
21 to 22
Thermal Diffusivity, mm2/s 7.3
11
Thermal Shock Resistance, points 20 to 35
20

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.040
Carbon (C), % 0 to 0.18
0 to 0.17
Chromium (Cr), % 11 to 13
0 to 0.3
Copper (Cu), % 0
0.5 to 0.8
Iron (Fe), % 84.5 to 89
95.1 to 97.2
Manganese (Mn), % 0 to 1.0
0.8 to 1.2
Molybdenum (Mo), % 0
0.25 to 0.5
Nickel (Ni), % 0
1.0 to 1.3
Niobium (Nb), % 0.050 to 0.3
0.015 to 0.045
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.25 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010

Comparable Variants