AISI 420 Stainless Steel vs. SAE-AISI 1108 Steel

Both AISI 420 stainless steel and SAE-AISI 1108 steel are iron alloys. They have 86% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 420 stainless steel and the bottom bar is SAE-AISI 1108 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 8.0 to 15
23 to 34
Fatigue Strength, MPa 220 to 670
170 to 260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 420 to 1010
250 to 280
Tensile Strength: Ultimate (UTS), MPa 690 to 1720
380 to 440
Tensile Strength: Yield (Proof), MPa 380 to 1310
220 to 360

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 620
400
Melting Completion (Liquidus), °C 1510
1460
Melting Onset (Solidus), °C 1450
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
52
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
1.8
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.0
1.4
Embodied Energy, MJ/kg 28
18
Embodied Water, L/kg 100
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88 to 130
95 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 4410
130 to 340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 62
13 to 16
Strength to Weight: Bending, points 22 to 41
15 to 16
Thermal Diffusivity, mm2/s 7.3
14
Thermal Shock Resistance, points 25 to 62
12 to 14

Alloy Composition

Carbon (C), % 0.15 to 0.4
0.080 to 0.13
Chromium (Cr), % 12 to 14
0
Iron (Fe), % 82.3 to 87.9
98.9 to 99.24
Manganese (Mn), % 0 to 1.0
0.6 to 0.8
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.75
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0.080 to 0.13