AISI 431 Stainless Steel vs. SAE-AISI 1070 Steel
Both AISI 431 stainless steel and SAE-AISI 1070 steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AISI 431 stainless steel and the bottom bar is SAE-AISI 1070 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 250 | |
| 190 to 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 15 to 17 | |
| 10 to 13 |
| Fatigue Strength, MPa | 430 to 610 | |
| 270 to 350 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Shear Strength, MPa | 550 to 840 | |
| 380 to 460 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1380 | |
| 640 to 760 |
| Tensile Strength: Yield (Proof), MPa | 710 to 1040 | |
| 420 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 850 | |
| 400 |
| Melting Completion (Liquidus), °C | 1510 | |
| 1460 |
| Melting Onset (Solidus), °C | 1450 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 26 | |
| 50 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.6 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 1.8 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 1.4 |
| Embodied Energy, MJ/kg | 31 | |
| 19 |
| Embodied Water, L/kg | 120 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 180 | |
| 59 to 86 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1270 to 2770 | |
| 470 to 850 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 32 to 50 | |
| 23 to 27 |
| Strength to Weight: Bending, points | 27 to 36 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 7.0 | |
| 14 |
| Thermal Shock Resistance, points | 28 to 43 | |
| 21 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.2 | |
| 0.65 to 0.75 |
| Chromium (Cr), % | 15 to 17 | |
| 0 |
| Iron (Fe), % | 78.2 to 83.8 | |
| 98.3 to 98.8 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.6 to 0.9 |
| Nickel (Ni), % | 1.3 to 2.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |