AISI 440A Stainless Steel vs. CC483K Bronze
AISI 440A stainless steel belongs to the iron alloys classification, while CC483K bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is AISI 440A stainless steel and the bottom bar is CC483K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 5.0 to 20 | |
| 6.4 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1790 | |
| 310 |
| Tensile Strength: Yield (Proof), MPa | 420 to 1650 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 170 |
| Melting Completion (Liquidus), °C | 1480 | |
| 990 |
| Melting Onset (Solidus), °C | 1370 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 370 |
| Thermal Conductivity, W/m-K | 23 | |
| 68 |
| Thermal Expansion, µm/m-K | 10 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.5 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 36 |
| Density, g/cm3 | 7.7 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 3.8 |
| Embodied Energy, MJ/kg | 31 | |
| 62 |
| Embodied Water, L/kg | 120 | |
| 400 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 120 | |
| 17 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 26 to 65 | |
| 9.9 |
| Strength to Weight: Bending, points | 23 to 43 | |
| 12 |
| Thermal Diffusivity, mm2/s | 6.2 | |
| 21 |
| Thermal Shock Resistance, points | 26 to 65 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.15 |
| Carbon (C), % | 0.6 to 0.75 | |
| 0 |
| Chromium (Cr), % | 16 to 18 | |
| 0 |
| Copper (Cu), % | 0 | |
| 85 to 89 |
| Iron (Fe), % | 78.4 to 83.4 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.7 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.6 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 10.5 to 13 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |